Sikaflex®-223
Weathering-resistant low-modulus adhesive sealant
Sikaflex®-223 is a low modulus 1-component polyurethane adhesive and sealant suitable for interior and exterior applications that bonds well to a wide variety of substrates. Its very good weathering resistance makes it suitable for exposed open joints, while its low elastic modulus allows the use of Sikaflex®-223 to bond and seal organic glasses (PC, PMMA).
- Good ageing and weathering resistance
- Suitable for bonding and sealing
- Easy to process and tool
- Suitable for a wide variety of organic glasses
PRODUCT BENEFITS
- Good ageing and weathering resistance
- Suitable for bonding and sealing
- Easy to process and tool
- Suitable for a wide variety of organic glasses
Usage
Sikaflex®-223 is a multi-purpose product for industrial sealing and bonding applications on most common substrates such as metals, GRP, 2-component coating and paint systems, plastics. Its very good weathering resistance makes it suitable for exposed open joints, while its low modulus allows the use of Sikaflex®-223 to bond and seal various organic glasses. Seek manufacturer’s advice and perform tests on original substrates before using Sikaflex®-223 on materials prone to stress cracking. This product is suitable for experienced professional users only. Tests with actual substrates and conditions have to be performed ensuring adhesion and material compatibility.Packaging
| Cartridge | 300 ml |
| Unipack | 600 ml |
| Pail | 23 l |
| Drum | 195 l |
Product Details
| Chemical base | 1-component polyurethane | |
| Color (CQP001-1) | Black, white | |
| Cure mechanism | Moisture-curing | |
| Density (uncured) | depending on color | 1.23 kg/l |
| Non-sag properties | Good | |
| Application temperature | ambient | 10 ─ 35 °C |
| Skin time (CQP019-1) | 60 minutes A | |
| Open time (CQP526-1) | 45 minutes A | |
| Curing speed (CQP049-1) | (see diagram) | |
| Shrinkage (CQP014-1) | 1 % | |
| Shore A hardness (CQP023-1 / ISO 48-4) | 35 | |
| Tensile strength (CQP036-1 / ISO 527) | 2 MPa | |
| Elongation at break (CQP036-1 / ISO 527) | 500 % | |
| Tear propagation resistance (CQP045-1 / ISO 34) | 5 N/mm | |
| Tensile lap-shear strength (CQP046-1 / ISO 4587) | 1.5 MPa | |
| Service temperature (CQP509-1 / CQP513-1) | -50 ─ 90 °C | |
| Shelf life | Unipack / Cartridge Pail / Drum | 12 months B 9 months B |
CQP = Corporate Quality Procedure | A) 23 °C / 50 % r. h. | B) storage below 25 °C |
CURE MECHANISM
Sikaflex®-223 cures by reaction with atmospheric moisture. At low temperatures the water content of the air is generally lower and the curing reaction proceeds somewhat slower (see diagram 1).
Diagram 1: Curing speed Sikaflex®-223
CHEMICAL RESISTANCE
Sikaflex®-223 is generally resistant to fresh water, seawater, diluted acids and diluted caustic solutions; temporarily resistant to fuels, mineral oils, vegetable and animal fats and oils; not resistant to organic acids, glycolic alcohol, concentrated mineral acids and caustic solutions or solvents.
Application
Surface preparation
Surfaces must be clean, dry and free from grease, oil, dust and contaminants.
Surface treatment depends on the specific nature of the substrates and is crucial for a long lasting bond.
Suggestions for surface preparation may be found on the current edition of the appropriate Sika® Pre-treatment Chart. Consider that these suggestions are based on experience and have in any case to be verified by tests on original substrates.
Application
Sikaflex®-223 can be processed between 10 °C and 35 °C (climate and product) but changes in reactivity and application properties have to be considered. The optimum temperature for substrate and sealant is between 15 °C and 25 °C. Consider that the viscosity will increase at low temperature. For easy application, condition the adhesive at ambient temperature prior to use.
To ensure a uniform thickness of the bondline it is recommended to apply the adhesive in form of a triangular bead (see figure 1).
Figure 1: Recommended bead configuration
Sikaflex®-223 can be processed with manual, pneumatic or electric driven piston guns as well as pump equipment. The open time is significantly shorter in hot and humid climate. The parts must always be installed within the open time. Never join bonding parts if the adhesive has built a skin.
For advice on selecting and setting up a suitable pump system, contact the System Engineering Department of Sika Industry.
Tooling and finishing
Tooling and finishing must be carried out within the skin time of the product. It is recommended using Sika® Tooling Agent N. Other finishing agents must be tested for suitability and compatibility prior the use.
Removal
Uncured Sikaflex®-223 may be removed from tools and equipment with Sika® Remover-208 or another suitable solvent. Once cured, the material can only be removed mechanically.
Hands and exposed skin have to be washed immediately using hand wipes such as Sika® Cleaner-350H or a suitable industrial hand cleaner and water.
Do not use solvents on skin.
Overpainting
Sikaflex®-223 can be painted after formation of a skin. If the paint requires a baking process, best performance is achieved by allowing the sealant to fully cure first. 1C-PUR and 2C-acrylic based paints are usually suitable. All paints have to be tested by carrying preliminary trials under manufacturing conditions.
The elasticity of paints is usually lower than that of sealants. This could lead to cracking of the paint in the joint area.